5754
EN AW / AlMg3 / 5754 / H34
Chemical Properties | % Value |
Silicon (Si) | 0,00 - 0,25 |
Chromium (Cr) | 0,05 - 0,20 |
Manganese (Mn) | 0,50 - 1,00 |
Magnesium (Mg) | 4,70 - 5,50 |
Copper (Cu) | 0,00 - 0,10 |
Titanium (Ti) | 0,00 - 0,20 |
Iron (Fe) | 0,00 - 0,40 |
Zinc (Zn) | 0,00 - 0,25 |
Aluminium (Al) | Balance |
Physical Properties | Value |
Density | 2,66 g/cm³ |
Melting Point | 568 °C |
Thermal Expansion | 23.9 x 10^-6 /K |
Modulus of Elasticity | 69 GPa |
Thermal Conductivity | 120 W/m.K |
Electrical Resistivity | %29 IACS |
Mechanical Properties | Value |
Proof Strength | 190 MPa |
Yield Strength | 260 MPa |
Elongation A50 mm | %11 |
Modulus of Elasticity | 69 GPa |
Aluminium alloy 5754 has excellent corrosion resistance especially to seawater and industrially polluted atmospheres.
ALLOY DESIGNATIONS
Aluminium alloy 5754 has similarities to the following standard designations and specifications ;
Alloy 5754 UNS A95754, ASTM B209
DIN AlMg3
TEMPER TYPES
5754 is supplied in a wide range of tempers:
- O - Soft
- H111 - Annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling.
- H112 - Applies to alloys that acquire some temper from shaping processes which do not have special control over the amount of strain-hardening or thermal treatment, but for which there are mechanical property limits.
- H28 - Strain-hardened and partially annealed - 4/4 hard (fully hardened).
- H32 - Work hardened by rolling then stabilised by low-temperature heat treatment to quarter hard
- H34 - Strain-hardened and stabilized - 1/2 hard.
- H36 - Strain-hardened and stabilized - 3/4 hard.
- H38 - Strain-hardened and stabilized - 4/4 hard (fully hardened).
SUPPLIED FORMS
5754 is supplied in plate, sheet, bar and extrusions.
- Plate
- Sheet
- Round Bar / Bar
- Tube / Extrusions